Titanium and its alloys are frequently used in dental and orthopedic implants because they have good mechanical strength, chemical stability and biocompatibility. These properties can be further improved by surface treatments such as anodization that are able to grow thicker and produce crystalline oxide layers with controlled morphological and physico-chemical properties. Both anatase (A) and rutile (R) crystalline phases of titanium oxide have been shown to promote bioactivity and antimicrobial effects. In a previous study in our laboratories, four electrolyte mixtures were optimized to produce anodized layers on commercially pure titanium consisting of specific anatase and rutile oxide ratios at an endpoint forming voltage of 180 V. In the present study, changes that occurred in the anodized layers with increasing forming voltage including crystallinity, thickness, surface morphology, surface roughness, surface chemistry, fractal dimension, shear strength, and corrosion resistance were determined for each of these electrolytes. The results showed the crystallinity, thickness, surface pore sizes, and surface roughness increased with increasing forming voltage. Incorporation of phosphorus into the anodized layers was shown in phosphoric acid containing electrolytes at higher forming voltages. Decreases in corrosion resistance were also shown at higher forming voltages in each electrolyte due to increased pore interconnectivity within the anodized layers. In addition, the apatite inducing ability of anodized layers in SBF was examined for selected forming voltages in each electrolyte. Anodization in phosphoric acid containing electrolytes was shown to be more favorable for apatite formation. The streptococcal and MRSA bacterial attachment before and after UV treatments was determined for selected forming voltages in each electrolyte. Additionally, the killing efficacy after 10-minute pre-irradiation with UVA or UVC treatments was determined. UVA treatments showed trends of at least a 20% reduction in bacterial attachment regardless of the crystallinity within the oxide for S. sanguinis. The anodized layer with an approximately equal distribution of anatase and rutile phases showed bacterial killing efficacy over 50% for S. sanguinis and over 80% for MRSA after UVA or UVC treatments. Finally, two forming voltage sample groups in two of the electrolytes were examined for MC3T3E-1 cell attachment, proliferation, and differentiation. Total intracellular protein content, alkaline phosphatase (ALP) activity, osteocalcin (OCN) activity, and cellular mineralization were investigated for different time periods up to 21 days. All sample groups showed suitable cellular proliferation, differentiation, and maturation but those anodized in the phosphoric acid containing electrolyte showed delayed proliferation and early differentiation and maturation. Also, anodized samples containing at least 50% anatase were shown to produce higher osteoblast mineralization compared to majority rutile phase anodized layers.