LE BUT DE CETTE THESE EST L'ETUDE DES PARAMETRES PHYSIQUES QUI FONT VARIER LES PROPRIETES ELECTRONIQUES ET MECANIQUES DES COUCHES MINCES DE CARBONE AMORPHE (A-C) EVAPOREES PAR LA TECHNIQUE DE DEPOSITION PAR LASER PULSE (PLD). TOUT D'ABORD, ON A FAIT DES EXPERIENCES POUR CONNAITRE LE SYSTEME EXPERIMENTAL: ON A ETUDIE LA COMPOSITION DU MATERIAU EVAPORE ET LA CINETIQUE DE DEPOSITION DES PARTICULES SUR LA SURFACE DE SI (111) 7X7. CETTE DERNIERE A ETE OBSERVE A L'ECHELLE ATOMIQUE AVEC UN MICROSCOPE A EFFET TUNNEL DANS L'ULTRA VIDE. DANS UNE DEUXIEME PARTIE, ON A CARACTERISE LES DEPOTS DE A-C. CES FILMS ONT UNE DENSITE ENTRE 2.45 G/CM#3 ET 2.8 G/CM#3 ET UNE DURETE JUSQU'A 50 GPA. ILS SONT SEMICONDUCTEURS AVEC UN GAP OPTIQUE DE 0.3 EV ET UNE RESISTIVITE ELECTRIQUE DE 10#5 CM. CES PROPRIETES SONT DEGRADEES SI L'ENERGIE CINETIQUE DES PARTICULES EVAPOREES EST DIMINUEE. L'ANALYSE PHYSICO-CHIMIQUE DE CES COUCHES MINCES A ETE FAITE EN UTILISANT LES SPECTROSCOPIES DE PHOTOEMISSION (XPS ET UPS), D'ABSORPTION DES RAYONS X (NEXAFS) ET RAMAN. CETTE ANALYSE REVELE QUE CES COUCHES SONT CONSTITUEES PAR DES ATOMES DE CARBONE HYBRIDES SP#2 ET SP#3. LA PROPORTION DES LIAISONS SP#3 PAR RAPPORT AUX LIAISONS SP#2 EST DE 40% POUR LES COUCHES DURES (45 GPA) ET 25% POUR LES MOINS DURES (22 GPA). LES RESULTATS NEXAFS OBTENUS EN DETECTION D'ELECTRON ET EN FLUORESCENCE SEMBLENT INDIQUER UN GRADIENT DE DENSITE DU MATERIAU, CELLE-CI AUGMENTANT DE LA SURFACE VERS LE VOLUME. FINALEMENT, LA SIMILITUDE OBSERVEE ENTRE LES SPECTRES RAMAN DE FILMS DE A-C AVEC DES DURETES SEMBLABLES MAIS DES GAP OPTIQUES RADICALEMENT DIFFERENTS INDIQUENT QUE LA SPECTROSCOPIE RAMAN EST PLUS SENSIBLE A L'ORGANISATION STRUCTURALE QU'AUX PROPRIETES ELECTRONIQUES DES DEPOTS DE A-C